Bimetallic Wear Plates
Bimetal steel plates are unique wear resistant materials in that they combine very high wear resistant qualities of a white iron (ASTM A532 15%CrMo, 700BHN – 63HRc) with a weldable &high impact toughness mild steel through a metallurgical bond to create a product that is exceptionally resistant to impact and abrasion while retaining. The typical property is as below:
Tensile Strength 630Mpa Min.
Shearing Strength 250Mpa Min.
Hardness 63 HRC/700BHN
The micro-structure is Carbide + Martensite + Retained Austenite, the carbide’s content is about 41.5%. The bimetallic wear plate, a component made by heavy forging, is widely used in feeder chute and hopper wear protection situations.
Why Choose WALKSON Bimetallic Wear Plates
Super high level wear-resistant ability
Custom made size to suit your need
Very stable brazing welding quality.